Neopox® CR – Waterproofing material for chemical tanks

Packing

Colors

Black

Trademark

Made in

Price: Contact

Solvent-free epoxy system, for applications that demand chemical resistance

Solvent-free epoxy system, for applications that demandchemical resistance

Applications :

Suitable for painting of tanks (internally) and surfaces in contact with chemicals, acids, bases, petrochemicals (not suitable for permanent contact with unleaded gasoline). It can be applied at shafts, sewage tanks in water treating facilities.

Technical Characteristics

Density                                                                     Component Α: 1,25-1,30gr/cm3
Component B: 0,94gr/cm3
Mixing ratio (by weight)                                         75A:25B
Consumption                                                           330-400gr/m2 per coat on a horizontal surface
280-330gm/m2 per coat on a vertical surface
Touch dry (+25oC)                                                  7 hours
Pot life                                                                     40 minutes at +25οC
60 minutes at +15 οC
(Low temperatures and humidity during application prolong the setting time, while high temperatures bring it
down)
Recoating (+25oC)                                                   24 hours
Application temperature                                           From +12C to +35C
Ambient humidity                                                     60-70%
Total hardening                                                         ~ 7 days
Adhesive strength                                                     > 2,5Ν/mm2

Packing and Storage stability:

    • Sets of 10kg
    • 3 years in sealed containers, provided that the 2 components are not mixed together

Instructions for use

Quality/Preparation of Substrate

The concrete substrate must be sound and of sufficient compressive strength (minimum 25 N/mm2) with a minimum pull off strength of 1.5 N/mm2.The substrate must be clean, dry (surface humidity content <4%) and free of all contaminants such as dirt, oil, grease, coatings and surface treatments, etc. Concrete substrates must be prepared mechanically using abrasive blast cleaning or scarifying equipment to remove cement laitance and achieve an open textured surface. Local putting can be achieved with Epoxol® Putty in proportion from 1Α:1B to 2A:1B or Epoxol® Primer SF mixed with quartz sand.

Instructions for use

The surface must be dry (humidity limit=5%). In concrete surfaces when the moisture of the substrate is up to 8%, if there is not rising moisture and the substrate temperature is > +12°C the surface should be primed with water-based primer Acqua® Primer. (All epoxy primers can be used e.g.Epoxol® Primer, Neopox® Primer 1225, Neopox® Primer WS, Neopox®Primer AY depending on the needs and the substrate). Application: Apply 1 coating of Νeopox® CR with brush, roller or airless gun. If the 2nd layer will be applied after 24 hours, lightly scrub the surface to roughen it

Notes

Νeopox® CR cannot be applied below +12οC
 
Colour: Black

Cleaning of tools

Immediately after application with solvent Neοtex® 1021.